TABLE X (Continued)

Silicon Dioxide (Glass)

eV	M-1	I'm	n	k

17.5	0.07085	0.999	0.750
17.25	0.07187	1.030	0.763
17	0.07293	1.072	0.768
16.75	0.07402	1.124	0.765
16.5	0.07514	1.137	0.755
16.25	0.07630	1.156	0.737
16	0.07749	1.172	0.717
15.75	0.07872	1.178	0.703
15.5	0.07999	1.172	0.696
15.25	0.08130	1.167	0.699
15	0.08266	1.168	0.711
14.75	0.08405	1.175	0.739
14.5	0.08551	1.195	0.771
14.25	0.08700	1.225	0.799
14	0.08856	1.265	0.808
13.75	0.09017	1.320	0.795
13.5	0.09184	1.363	0.775
13.25	0.09357	1.371	0.755
13	0.09537	1.368	0.747
12.75	0.09724	1.372	.0.766
12.5	0.09919	1.383	0.793
12.25	0.1012	1.410	0.824
12	0.1033	1.475	0.861
11.8	0.1051	1.554	0.874
11.6	0.1069	1.635	0.859
11.4	0.1088	1.716	0.810

	11.2	0.1107	1.766 [9]	0.718 [12]
11	0.1127	1.739	0.569
	10.9	0.1137	1.687	0.565
	10.8	0.1148	1.587	0.618
	10.7	0.1159	1.513	0.725
	10.6	0.1170	1.492	0.914
	10.5	0.1181	1.567	1.11
	10.45	0.1187	1.645	1.136
	10.4	0.1192	1.772	1.13
	10.35	0.1198	1.919	1.045
	10.3	0.1204	2.048	0.925
	10.25	0.1210	2.152	0.810
	10.2	0.1215	2.240	0.715
	10.1	0.1228	2.332	0.460
	10	0.1240	2.330	0.323
	9.9	0.1252	2.292	0.236
	9.8	0.1265	2.243	0.168
	9.7	0.1278	2.190	0.119
	9.6	0.1291	2.140	0.077
	9.5	0.1305	2.092	0.0561 [12-14]
	9.4	0.1319	2.047	0.0430